A387Gr11CL2,A387Gr12CL2 steel plate

          A387Gr11CL2,A387Gr12CL2 steel plate

1.Application Potential:

     A387/A387M specification covers chromium-molybdenum alloy steel plates intended primarily for welded boilers and pressure vessels designed for elevated temperature service.This standard covers steel A387Gr2CL1, A387Gr2CL2,A387Gr12CL1,A387Gr12CL2A387Gr11CL1,A387Gr11CL2,A387Gr22CL1,A387Gr22CL2,A387Gr21CL1,A387Gr21CL2,A387Gr5CL1,A387Gr5CL2,A387Gr9CL1,A387Gr9CL2,A387Gr21LCL1,A387Gr22LCL1and A387Gr91CL2.These plates are widely used in the fabrication of boilers and pressure vessels in industries such as shipbuilding, petrochemical and manufacturing.

2.Chemical Composition and Mechnical Property:

Chemical composition

Grade	Standard	C	Mn	S	P	Si
A387Gr11CL2	A387/A387M	0.04-0.17	0.35-0.73	0.035	0.035	0.44-0.86
A387Gr12CL2	A387/A387M	0.04-0.17	0.35-0.73	0.035	0.035	0.13-0.45

Mechnical Property

Grade	Tensile strength, ksi [MPa]	Yield strength, min,A ksi [MPa]	Elongation in 8 in. [200 mm], min, %B	Elongation in 2 in. [50 mm], min, %B
A387Gr11CL2	60 to 85 [415 to 585]	35 [240]	19	22
A387Gr12CL2	55 to 80 [380 to 550]	33 [230]	18	22

3.A387Gr11CL2,A387Gr12CL2 material shall have a coarse austenitic grain size.They shall be thermally treated either by annealing, normalizing- and -tempering, or, when

permitted by the purchaser, accelerated cooling from the austenitizing temperature by air blasting or liquid quenching,followed by tempering. Minimum tempering temperatures

shall be 620°C.For more Supplementary requirements such as S1. Vacuum Treatment,S2. Product Analysis and so on,do not hesitate to contact us,we will do our best to satisfy you.