1.Application Potential:
A537 specification covers heat-treated carbonmanganese-silicon steel plates intended for fusion welded pressure vessels and structures.Material under this specification is available in the
following three classes:A537CL1,A537CL2,A537CL3.They are widely used in boiler and pressure vessel building.
2.Chemical Composition and Mechnical Property:
Chemical composition
Grade
|
Standard
|
C
|
Mn
|
S
|
P
|
A537CL1,A537CL2
|
A537/A537M
|
0.38
|
0.92-1.72
|
0.13-0.55
|
0.035
|
Mechnical Property
Grade
|
Tensile strength, ksi [MPa]
|
Yield strength, min,A ksi [MPa]
|
Elongation in 2 in. [50 mm], min, %B
|
Elongation in 8 in. [200 mm], min, %B
|
A537CL1
|
65–85
[450–585]
|
45 [310]
|
22
|
18
|
A537CL2
|
70–90 [485–620]
|
55 [380]
|
20
|
C
|
3. Class 1 plates shall be normalized.Class 2 and Class 3 plates shall be quenched and
tempered. The tempering temperature for Class 2 plates shall not be less than 1100°F [595°C] for not less than 1⁄2 h and 1150°F [620°C] for Class 3 plates for not less than 1⁄2 h.
Contact :
Email: nina@hzzsteel.com.cn
Sales: Nina Zhang
Gmail: hzzsteel5@gmail.com
Msn: hzzsteel5@hotmail.com
Skype: hzzsteel5
T:86-371-65862331
F:86-371-65652677
Cell:86-13603980267
No comments:
Post a Comment